The Paton Welding Journal, 2007, #7, 35-39 pages
Application of corrision-resistant surfacing in technological equipment operating in contact with sea water
A.S. Salnikov, V.V. Otrokov, G.M. Shelenkov, E.A. Tsymbal, M.A. Laktionov
OJSC «M.V. Frunze Sumy NPO», Sumy,Abstract
The results are given on comparative testing of anticorrosion deposits used for protection of power generation equipment operating in sea water. KhN65MV (EP-567) alloy has the highest pitting corrosion resistance in sea water. As to tribotechnical parameters, KhN65MV alloy in contact with FUT coal-plastic is inferior to FUT + bronze pair. KhN65MV alloy can be recommended for protection from pitting and contact corrosion of low-load components operating under the conditions of their wetting by sea water.
Keywords: arc surfacing, technological equipment, power generation systems, corrosion failure, corrosion-resistant surfacing, deposited metal, tribotechnical tests, deformation hardening, pitting corrosion
References
1. Ulianin, E.A. (1991) Corrosion-resistant steels and alloys: Refer. Book. Moscow: Metallurgiya.2. Voronenko, B.I. (1995) Corrosion resistance of current austenitic-ferritic (duplex) stainless steels. Special types of corrosion (Review). Zashchita Metallov, 31(2).
3. (1987) Corrosion: Refer. Book. Ed. by L.L. Shrajer. Moscow: Metallurgiya.
4. Chendler, K.A. (1988) Corrosion of vessels and marine structures. Leningrad: Sudostroenie.
5. Kravtsov, T.G., Kravtsov, V.T. (2004) New surfacing material for recovery and corrosion protection of shafts under cyclic loading service conditions. In: Proc. of 3rd Int. Conf. on Welding Consumables. Dnepropetrovsk.
6. (1983) Sea corrosion. Ed. by N.N. Shumakher. Moscow: Metallurguya.
7. Chukalovskaya, T.V., Shcherbakov, A.I., Chigirinskaya, L.A. et al. (1995) Corrosion-electrochemical behavior of electrode pairs of coal-plastic-metal in corrosive media. Zashchita Metallov, 31(2).
8. (1974) USSR register: Rules of classification of sea vessel construction. Vol. 2. Leningrad: Transport.
9. (1975) Materials for short-term seminar of September, 29–30, 1975. Ed. by Yu.M. Belov, A.E. Vajnerman. Leningrad.
10. Babaev, A.N. (1975) About conditions of conducting fatigue and corrosion-fatigue tests of specimens and transferring their results to real propeller shafts with a deposit. In: Materials for short-term seminar of September, 29–30, 1975. Leningrad.
11. Khaet, G.L., Stenko, D.A., Brusilovsky, B.A. (1959) Experience of Novokramatorsk Machine-Building Works on roller treatment of large parts: Transact. of TsNIITMASh. Moscow: Mashgiz.
12. Polevoj, S.N., Evdokimov, V.D. (1986) Hardening of metals: Refer. Book. Moscow: Mashinostroenie.
13. Tochilnikov, D.G., Ginzburg, B.M. (2002) Procedure of fast tests of antifriction polymers. Voprosy Materialovedeniya, 31(3).
14. OST 5.9573-84: Surfacing shipbuilding carbon and alloyed steels with aluminium bronzes, copper-nickel alloy and corrosion-resistant steels. Standard technological process, acceptance rules and testing methods.
15. OST 26-01-858-94: Welded vessels and apparatuses of nickel and corrosion-resistant alloys on nickel base. General specifications.
16. Anisimov, A.V., Bakhereva, V.E. et al. (2002) Study of the influence of mating body material on indices of coal-plastics at friction with water wetting. Voprosy Materialovedeniya, 31(3).