Avtomatichne Zvaryuvannya (Automatic Welding), #11, 2019, pp.46-51
Pecularities of electron beam welding of hot-rolled aluminum-lithium alloys
D. Drimal, M. Kasencak, F. Kolenic, A. Kramarcik, L. Kovac
PRVA ZVARACSKA a. s. Kopcianska 14, 85101, Bratislava, Slovak Republic. E-mail: firstname.lastname@example.org
This paper presents results of experiments on electron beam welding of Al–Li alloys. The wrought AW 2099 alloy was used as experimental material. AW 2099 alloy in T83 condition of thickness 25 mm was used. The microstructure of experimental alloy was degraded by annealing and deformation before welding. The original thickness 25 mm was reduced to 3 mm by hot rolling without any subsequent additional heat treatment. The full penetration butt-welds and T-joint configurations were made by electron beam. These welded joints underwent investigation of basic mechanical testing (tensile strength, bending, hardness) and metallographic inspection for internal defects and microstructure identification. Welded joints didn’t have significant internal defects, but tensile strength and plastic properties were deteriorated significantly by welding process and previous deformation. The heat treatment was performed for improvement of mechanical and plastic properties. The heat treatment mode consists of solution treatment (annealing) followed by quenching and subsequent aging cycles. 5 Ref., 5 Tabl., 8 Fig.
Keywords: aluminum-lithium alloys, electron beam welding, macrostructure of weld, tensile strength test
References1. Hrivňák, I. Zváranie a zvariteľnosť materiálov. (2009) V Bratislave: Slovenská technická univerzita. Edícia vysokoškolských učebníc. ISBN 978-80-227-3167-6.
2. Metalwebnews: Lithium aluminium alloys - the new generation aerospace alloys. Metal Web News, ©2007 https://web.archive.org/web/20070928094349/http:/www.metalwebnews.com/howto/alloys/alloys.pdf
3. Lin Y., Z.Q. Zheng and S.C. Li. (2013) Effect of solution treatment on microstructures and mechanical properties of 2099 Al-Li alloy. [cit. 2019-01-24]. https://doi.org/10.1016/j.acme.2013.07.005
4. Rioja, Roberto J. and John Liu. (2012) The evolution of Al-Li base products for aerospace and space applications. Metallurgical and Materials Transact. A. Springer US, 43(9), 3325-3337. https://doi.org/10.1007/s11661-012-1155-z
5. Wang, S., Y. Huang and L. Zhao. (2017) Effects of different aging treatments on microstructures and mechanical properties of Al-Cu-Li alloy joints welded by electron beam welding. [cit. 2019-01-24]. https://doi.org/10.1016/j.cja.2017.07.002