Avtomaticheskaya Svarka (Automatic Welding), #11, 2022, pp. 12-17
Recovery and recrystallization of metal of steam line welded joints during long-term service
V.V. Dmytryk, I.V. Kasyanenko, Yu.M. Latynin
NTU «Kharkiv Polytechnic Institute». 2 Kyrpychova Str., 61002, Kharkiv, Ukraine. E-mail: igorkasyanen@gmail.com
The processes of recovery and recrystallization occur in the metal of welded joints of heat-resistant pearlitic steels at their long-term operation. The running of these processes is very different from similar processes taking place at normal annealing. At recrystallization proceeding in the welded joint metal, some intergranular boundaries disappear, and the formed grains take an elongated shape. A decrease of strength by approximately 10…15 and of impact toughness by 15…18 % is observed in the recrystallized metal. It is found that recovery and recrystallization as components of the overall process of transformation of the initial structure of welded joint metal into a ferrite-carbide mixture proceed at its plastic deformation. The distribution of vacancies changes during recrystallization, differing essentially in the HAZ subzones. The highest deformation level is observed in the incomplete recrystallization subzone of the HAZ. Studying the features of recovery and recrystallization processes is relevant for determination of the reliability of operation and life of welded joints, as well as development of new heat-resistant steels, which will operate at higher working parameters – temperature and time. 11 Ref., 13 Fig.
Keywords: welded joints, heat-resistant steels, recovery, recrystallization, life, creep conditions, structural phase state, mechanical propertiesі
Received: 24.06.2022
References
1. GKD 34.17.401-95. Inspection and extension of service life of metal of thermal power plant equipment. Standard instruction. Pt. 1. Boilers, turbines and pipelines with pressure of 9 MPa and higher [in Ukrainian].2. DNAOP 0.00-1.11-98. Rules of construction and safe operation of steam and hot water lines [in Ukrainian].
3. Indenbaum, G.V., Rozenberg, V.Yu. (1986) Recovery and recrystallization of metals. Moscow, Metallurgiya
4. Dmytryk, V.V., Kasyanenko, L,V., Latynin, Yu.M. (2021) Structural state and damageability of welded joint metal of steam pipelines. The Paton Welding J., 9, 1-5 (нема в цьому році і в цьому номері)
5. Khromchenko, F.A. (2002) Life of welded joints of steam pipelines. Moscow, Mashinostroenie [in Russian].
6. Glushko, A.V., Dmitrik, V.V., Syrenko, T.A. (2018) Creep of welded joints of steam pipelines. Metallofizika. Novejshie Tekhnologii, 40(5), 683-700 [in Russian]. https://doi.org/10.15407/mfint.40.05.0683
7. Dmitrik, V.V., Tsaryuk, A.K., Konyk, A.I. (2008) Carbide phases and damageability of welded joints of steam pipelines under creep conditions. The Paton Welding J., 3, 28-32.
8. (2002) Viability of steam pipelines of aging thermal power plants. Eds by Yu.L. Izrailev, F.A.Khromchenko, Moscow, TORUS-PRESS [in Russian].
9. Krechkovska, G.V., Student, O.Z., Svirska, L.M. (2017) Heterogeneous distribution of carbides in structure of used steel 12Kh1MF from different zones of steam bypass line of main TPP pipelines. Naukovi Notatky, 59, 154-158 [in Ukrainian].
10. Dmitrik, V.V., Glushko, A.V., Sirenko, T.O. (2017) Structural changes in metal of welded joints of steam pipelines. The Paton Welding J., 7, 15-18. https://doi.org/10.15407/tpwj2017.07.03
11. Skulsky V.Yu., Tsaryuk, A.K. (2004) New heat-resistant steels for manufacture of weldments on heat power units (Review). The Paton Welding J., 4, 32-37.
Advertising in this issue: