Electrometallurgy Today (Sovremennaya Elektrometallurgiya), 2023, #4, 5-9 pages

Nickel scrap recycling by electron beam melting method

S.V. Akhonin1, V.O. Berezos1, O.G. Erokhin2, O.O. Kotenko2, M.I. Medvedev3, M.G. Lyashenko4

1E.O. Paton Electric Welding Institute of the NAS of Ukraine 11 Kazymyr Malevych Str., 03150, Kyiv, Ukraine. E-mail: office@paton.kiev.ua
22SC «SPC «Titan» of the E.O.Paton Electric Welding Institute of the NAS of Ukraine». 26 Raketna str., 03028, Kyiv, Ukraine. E-mail: titan.paton@gmail.com
3Ukrainian State University of Science and Technologies. 2 Lazaryan Str., 49010, Dnipro, Ukraine. Е-mail: michael.medvedev4747@gmail.com
4«DZST» Ltd. 1 Horyanivska Str., Horyanivske vil., 52035, Dnipropetrovsk region, Ukraine. Е-mail: mirdzst@i.ua

Abstract
Experimental-industrial melting of low-grade nickel scrap was conducted to obtain nickel ingots of not lower than NP2 grade, which are furtheron used to produce semi-finished products in the form of hot- and cold-formed seamless pipes, including capillary, thin-walled and particularly thick-walled, rings, squares, hexagons, etc. It is shown that during electron beam melting a significant removal of impurity elements from the nickel scrap occurred, and metal quality began to correspond to nickel grade not lower than NP2. In order to further study the produced ingot quality, comprehensive research work was performed on manufacturing semi-finished products in the form of elongated soft rods of 40 mm diameter and wire of 3 mm diameter. It was determined that mechanical properties of semi-finished products from EBM nickel fully meet the standard requirements. It is shown that electron beam melting is an efficient method of producing nickel ingots from secondary raw materials, as it allows ensuring a high level of the produced material quality, and the semi-finished product quality fully meets the standard requirements by chemical composition, structure and mechanical properties. 9 Ref., 2 Tabl., 6 Fig.
Keywords: electron beam melting, electron beam unit, nickel, melting, ingot, scrap, refining

Received 31.10.2023

References

1. Grytsai, V.P., Bredykhin, V.M., Chervonyi, I.F. et al. (2010) Metallurgy of nonferrous metals: Manual. Pt 5. Book 2, Technology of copper and nickel. Ed. by I.F. Chervonyi. Zaporizhzhiya, ZDIA [in Ukrainian].
2. Pozhuev, V.I., Ivashchenko, V.I., Chervonyi, I.F., Grytsai, V.P. (2007) Metallurgy of nonferrous metals: Manual. Pt 1. Ed. by I.F. Chervonyi. Zaporizhzhiya, ZDIA [in Ukrainian].
3. Paton, B.E., Trigub, N.P., Akhonin, S.V., Zhuk, G.V. (2006) Electron beam melting of titanium. Kyiv, Naukova Dumka [in Russian].
4. Dmitrenko, A.E., Kozhevnikov, O.E., Pelykh, V.N. (2003) Application of method of electron beam melting for refining of nickel. Voprosy Atomnoj Nauki i Tekhniki, 5, 162–166 [in Russian].
5. Azhazha, V.M., Zejdlits, M.P., Shevchenko, S.V., Amonenko, V.M. (1973) Influence of chemically active elements on properties of nickel of electron beam melting. Izv. AN SSSR. Metally, 4, 157–159 [in Russian].
6. Trigub, N.P., Berezos, V.A., Kornijchuk, V.D., Mosunov, Yu.A. (2011) Producing of high-quality nickel ingots-slabs by electron beam melting. Advances in Electrometallurgy, 2, 78–81.
7. Movchan, B.A., Tikhonovsky, A.L., Kurapov, Yu.A. (1973) Electron beam melting and refining of metals and alloys. Kyiv, Naukova Dumka [in Russian].
8. Akhonin, S.V., Pikulin, A.N., Berezos, V.A. et al. (2019) Laboratory electron beam unit UE-208M. Sovrem. Elektrometal., 3, 15-22 [in Russian]. https://doi.org/10.15407/sem2019.03.03
9. GOST 13083–77: Rods from nickel and silicon nickel. Specifications.

Advertising in this issue: