TPWJ, 2017, #7, 43-47 pages
 
Influence of preheating parameters and local heat treatment on structure and properties of dispersion-strengthened joints of silicon-containing titanium alloys made by electron beam welding


Journal                    The Paton Welding Journal
Publisher                 International Association «Welding»
ISSN                      0957-798X (print)
Issue                       #7, 2017 (July)
Pages                      43-47
 
 
Authors
S.V. Akhonin, E.L. Vrzhizhevsky, V.Yu. Belous and I.K. Petrichenko
E.O. Paton Electric Welding Institute, NASU 11 Kazimir Malevich Str., 03680, Kiev, Ukraine. E-mail: office@paton.kiev.ua
 
Abstract
Titanium alloys have high strength and corrosion resistance in a broad temperature range. When developing promising alloys, it is necessary to increase both working temperatures of parts and components of future engines, and their specific strength. The work is a study of the influence of preheating and local heat treatment on the structure and properties of EB welded joints of experimental silicon-containing titanium alloys, namely pseudo a-alloy Ti–5.6Al–2.2Sn–3.5Zr–0.4Mo–1V–0.6Si and (a + b)-alloy Ti–4.3Al–4.4Sn–6Zr–1.6Mo–0.7V–4.3Nb–0.4Si. Welded joints of dispersion-strengthened titanium (a + b)-alloy Ti–4.3Al–4.4Sn–6Zr–1.6Mo–0.7V–4.3Nb–0.4Si have higher ultimate strength, reaching 1277 MPa that corresponds to 90 % of that of the alloy proper. Long-term strength s100 at 600 °C temperature of welded joint of Ti–4.3Al–4.4Sn–6Zr–1.6Mo–0.7V–4.3Nb–0.4Si titanium alloy is equal to about 260 MPa that is on the level of 93 % of long-term strength of base metal. 12 Ref., 4 Figures, 3 Tables.
 
Keywords: titanium, titanium alloy, dispersion strengthening, electron beam welding, structure, properties, strength, long-term strength
 
 
Received:                15.05.17
Published:               01.09.17
 
 
References
  1. Mukhin, V.S. (2007) Principles of technology of machine building (aircraft engine building). Ufa: UGATU.
  2. Ilienko, V.M., Shalin, R.E. (1995) Titanium alloys for aircraft gas-turbine engines. Titan (VILS), 1/2, 25.
  3. Iliin, A.A., Kolachev, B.A., Polkin, I.S. (2009) Titanium alloys. Composition, structure, properties: Refer. Book. Moscow: VILS-MATI.
  4. Ivanov, V.I., Yasinsky, K.K. (1996) Efficiency of application of heat-resistant alloys based on Ti3Al and TiAl intermetallics for operation at temperatures of 600–800 oC in aerospace engineering. Tekhnologiya Lyogkikh Splavov, 3, 12–25.
  5. Solonina, O.P., Glazunov, S.G. (1996) Heat-resistant titanium alloys: Refer. Book. Moscow: Metallurgiya.
  6. Levitsky, N.I., Matvinets, E.A., Lapshuk, T.V. et al. (2012) Producing complex-doped titanium alloys by method of electron beam skull melting. Metall i Lityo Ukrainy, 4, 6–9.
  7. Vrzhizhevsky, E.L., Sabokar, V.K., Akhonin, S.V. et al. (2013) Influence of local heat treatment at EBW of titanium alloys with silicide strengthening on mechanical properties of weld metal. The Paton Welding, J., 2, 20–23.
  8. Lyasotskaya, V.S., Lysenkov, Yu.T., Gerasimenko, A.V. et al. (1985) Influence of local heat treatment on structure and properties of VT6ch alloy welded joints. Avitsionnaya Promyshlennost, 11, 57–59.
  9. Anoshkin, N.F., Sigalov, Yu.M. (2002) Titanium alloys with higher heat resistance. Tekhnologiya Lyogkikh Splavov, 1, 38–50.
  10. Zvikker, U. (1979) Titanium and its alloys. Moscow: Metallurgiya.
  11. Kornilov, I.I., Budberg, P.B. (1961) State diagrams of binary and ternary systems. Moscow: VINITI.
  12. Markashova, L.I., Akhonin, S.V., Grigorenko, G.M. et al. (2012) Structure and properties of welded joints on titanium alloys containing silicon additions. The Paton Welding J., 11, 6–15.