The Paton Welding Journal, 2003, #9, 11-14 pages

Assessment of technological strength of plate hardenable steel joints with multilayer welds

A.T. Nazarchuk, V.V. Snisar, Yu.A. Zaburanny

E.O. Paton Electric Welding Institute of the NASU 11 Kazymyr Malevych Str., 03150, Kyiv, Ukraine.

Abstract
Peculiarities in the development of a new approach to assessment of technological strength of hardenable steel joints with multilayer welds are considered. On their basis the feasibility of application of a method of composite specimens for assessment of not only weld metal, but also welded joint as a whole, has been substantiated and confirmed experimentally.
Keywords: hardenable steels, technological strength, cold cracks, test methods, instrument methods, technological samples

References

1. (1974) Technology of fusion electric welding of metals and alloys. Ed. by B.E. Paton. Moscow: Mashinostroenie.
2. Makara, A.M., Mosendz, N.A. (1971) Welding of highstrength steels. Kyiv: Tekhnika.
3. Makarov, E.L. (1981) Cold cracks. Moscow: Mashinostroenie.
4. Shorshorov, M.Kh. (1965) Metals science of welding of steel and titanium. Moscow: Nauka.
5. Kasatkin, S.B., Mikhoduj, L.I., Gordonny, V.G. (1996) Procedural approaches to complex investigation of delayed and brittle fracture of welded joints from high-strength lowalloy steels. Avtomatich. Svarka, 2, 58-60.
6. Kasatkin, B.S., Brednev, V.I., Tsaryuk, A.K. et al. (1993) Evaluation of resistance of 15Kh2MFA steel welded joints to cold cracking. Ibid., 5, 3-7.
7. Tsaryuk, A.K., Brednev, V.I. (1998) About problem of nature of cold cracking in welding of hardenable steels. Ibid., 10, 9-13.
8. Tsaryuk, A.K., Brednev, V.I. (1996) Problems of cold crack prevention. Ibid., 1, 36-40.
9. Kasatkin, B.S., Brednev, V.I. (1985) Peculiarities of mechanism of cold crack formation in welded joints of highstrength steels. Ibid., 8, 1-6, 18.
10. Mikhoduj, L.I., Poznyakov, V.D., Yushchenko, A.K. (2000) Resistance of 12KhGN2MFDRA steel welded joints to a delayed fracture. The Paton Welding J., 11, 4-10.
11. Musiyachenko, V.F., Kasatkin, S.B. (1985) Hydrogen distribution in alloy steel welded joint and its influence on cold crack formation (Review). Avtomatich. Svarka, 9, 3-8.
12. Pokhodnya, I.K., Shvachko, V.I. (1997) Physical nature of hydrogen-induced cold cracks in structural steel welded joints. Ibid., 5, 3-12.
13. Pokhodnya, I.K., Stepanyuk, S.N., Shvachko, V.I. (2000) Role of temperature in hydrogen-induced cracking of structural steels and welded joints. The Paton Welding J., 2, 2-7.
14. Nazarchuk, A.T., Sterenbogen, Yu.A., Kosyakov, V.P. (1984) Procedure of evaluation of weld metal susceptibility to longitudinal cracking. Avtomatich. Svarka, 12, 7-10.
15. Nazarchuk, A.T., Sverdel, I.P. (1994) Resistance of hardenable steel joints with multilayer welds to cracking. Ibid., 1, 15-19.
16. Nazarchuk, A.T., Kosyakov, V.P. Method of testing of hardenable steel welded joints on cold cracking susceptibility. USSR author’s cert. 1585709. Int. Cl. G 01 3/00. Publ. 15.08.90.
17. Shlepakov, V.N., Giyuk, S.P. (1987) Application of beadon-plate slot sample for determination of influence of hydrogen on cold cracking. Avtomatich. Svarka, 4, 37-39.
18. Sterenbogen, Yu.A., Bursky, G.V. (1987) Method of evalu¬ation of resistance of high-strength steel welded joint HAZ to cold cracking. Ibid., 3, 1-5.
19. Snisar, V.V., Demchenko, E.L., Ivanchenko, E.V. (2000) Challenging technologies for high-strength steel welding without preheating and heat treatment. The Paton Welding J., 11, 37-40.

---

Suggested Citation

A.T. Nazarchuk, V.V. Snisar, Yu.A. Zaburanny (2003) Assessment of technological strength of plate hardenable steel joints with multilayer welds. The Paton Welding J., 09, 11-14 .

---