The Paton Welding Journal, 2022, #5, 26-32 pages

Argon-arc welding of high-temperature titanium alloy doped by silicon

S.V. Akhonin, V.Yu. Bilous, R.V. Selin, I.K. Petrychenko, L.M. Radchenko, S.B. Rukhanskyi


E.O. Paton Electric Welding Institute of the NASU. 11 Kazymyr Malevych Str., 03150, Kyiv, Ukraine. E-mail: akhonin.sv@gmail.com

Abstract
Welding of titanium alloys doped by silicon requires application of additional technological operations, such as local heat treatment and preheating. In view of the fact that tungsten electrode argon-arc welding became widely applied in industry, the possibility of application of preheating for argon-arc welding of high-temperature pseudo-α titanium alloy of Ti‒5.6A1‒2.2Sn‒3.5Zr‒0.4Mo‒1.0V‒0.6Si system was studied. In the work, preheating of the joints to the temperatures of 200 and 400 °C was used. The temperature of preheating before welding in the range of 200‒400 °C does not influence the final microstructure of the produced welded joints. AAW-joints of high-temperature pseudo-α Ti‒5.6Al‒2.2Sn‒3.5Zr‒0.4Mo‒l.0V‒0.6Si alloy, produced with the preheating to 400 °C, have the highest ultimate tensile strength on the level of σt = 1160.1 MPa, impact toughness values of samples with a sharp notch are on the level of 8.3 J/cm2.
Keywords: titanium, titanium alloys, dispersion hardening, high-temperature pseudo-α titanium alloy, argon-arc welding, structure, properties, strength

Received: 15.04.2022
Accepted: 08.08.2022

References

1. Mukhin, V.S. (2007) Fundamentals of mechanical engineering technology (aircraft engine building0. Ufa, UGATU [in Russian].
2. Ilienko, V.M., Shalin, R.E. (1995) Titanium alloys for aircraft gas turbine engines. Titan (VILS), 1-2 [in Russian].
3. Iliin, A.A., Kolachev, B.A., Polkin, I.S. (2009) Titanium alloys. Composition, structure, properties: Handbook. Moscow, VILS MATI [in Russian].
4. Ivanov, V.I., Yasinsky, K.K. (1996) Efficiency of application of heat-resistant alloys based on intermetallics Ti3Al and TiAl for operation at 600-800 oC temperatures in aerospace engineering. Tekhnologiya Lyogkikh Splavov, 3.
5. Solonina, O.P., Glazunov, S.G. (1996) Heat-resistant titanium alloys: Handbook. Moscow, Metallurgiya [in Russian].
6. Makarov, E.L. (1981) Cold cracks in welding of alloyed steels. Moscow, Mashinostroenie [in Russian].
7. Akhonin, S.V., Belous, V.Yu. (2017) Argon-arc welding of titanium and its alloys using fluxes (Review). The Paton Welding J., 2, 7-12. https://doi.org/10.15407/tpwj2017.02.02
8. Guseva, E.A., Klimychev, A.I. (1997) Through penetration argon-arc welding of titanium alloys. Svarochn. Proizvodstvo, 2, 15-16 [in Russian].
9. Gurevich, S.M. (1990) Handbook on welding of nonferrous metals. Kyiv, Naukova Dumka [in Russian].
10. Akhonin, S.V., Vrzhizhevsky, E.L., Belous, V.Yu., Petrichenko, I.K. (2017) Influence of preheating parameters and local heat treatment on structure and properties of dispersion-strengthened joints of silicon-containing titanium alloys made by electron beam welding. The Paton Welding J., 7, 43-47. https://doi.org/10.15407/tpwj2017.07.09
11. Levitsky, N.I., Matvinets, E.A., Lapshuk, T.V. et al. (2012) Producing of complex titanium alloys by method of electron beam skull melting. Metall i Litio Ukrainy, 4, 6-9 [in Russian].
12. Anoshkin, N.F., Sigalov, Yu.M. (2002) Titanium alloys with higher heat resistance. Tekhnologiya Lyogkikh Splavov, 1, 38-50 [in Russian].

Suggested Citation

S.V. Akhonin, V.Yu. Bilous, R.V. Selin, I.K. Petrychenko, L.M. Radchenko, S.B. Rukhanskyi (2022) Argon-arc welding of high-temperature titanium alloy doped by silicon. The Paton Welding J., 05, 26-32.