Influence of parameters of magnetron sputtering process on phase composition and structure of carbon nitride coatings

Yu.S. Borysov1, O.V. Volos1, N.V. Vigilyanska1, V.G. Zadoya1, V.V. Strelchuk2


1E.O. Paton Electric Welding Institute of the NASU. 11 Kazymyr Malevych Str., 03150, Kyiv, Ukraine. E-mail: pewinataliya@gmail.com
2V.E. Lashkaryov Institute of Semiconductor Physics of the NAS of Ukraine. 45 Nauki Ave., 02000, Kyiv, Ukraine

Abstract
Sputtering of CNx-coatings was carried out using two magnetron devices with titanium and graphite targets in the mixture of Ar/N2 gases. The influence of gas mixture (Ar/N2) composition, pressure (0.35, 1 and 2 Pa) and temperature (100…200 °C) on the structure of CNx coatings were investigated. It was found that the structure of the coating has an amorphous disordered graphite-like structure with sp3-, sp2- and sp1 electron bonds of carbon. The most ordered structure is observed in CNx coatings (the least ID/IG = 1.16 and 1.2), produced at a pressure of 0.35 Pa, the temperature of the specimen is 130 °C, the content of nitrogen is 40 and 58%. The influence of a titanium sublayer and a transition TiCN layer on adhesive properties of CNx coatings was studied. When a titanium sublayer and a transition TiCN layer are used together, the adhesion of the coating to the bases of titanium and Kh18N10Т steel grows at a thickness of coating being 2...3 μm. 15 Ref., 2 Tabl., 6 Fig.
Keywords: magnetron sputtering, CNx coating, structure, phase composition, Raman spectroscopy

Received: 04.07.2022
Accepted: 11.11.2022

References

1. Hultman, L., Neidhardt, J., Hellgren, N. et al. (2003) Fullerenelike Carbon Nitride: A Resilient Coating Material. MRS Bulletin, 28(03), 194-202. https://doi.org/10.1557/mrs2003.62
2. Liu, A.Y., Cohen, M.L. (1989) Prediction of New Low Compressibility Solids. Science, 245(4920), 841-842. https://doi.org/10.1126/science.245.4920.841
3. Liu, D., Ruan, C.F., Zhang, P. et al. (2021) Structural, interface texture and toughness of TiAlN/CN multilayer films. Materials Characterization, 178, 111301. https://doi.org/10.1016/j.matchar.2021.111301
4. Vyas, A., Shen, Y., Zhou, Z., Li, K. (2008) Nano-structured CrN/CNx multilayer films deposited by magnetron sputtering. Composites Science and Technology, 68(14), 2922-2929. https://doi.org/10.1016/j.compscitech.2007.11.002
5. Nishimura, H., Umehara, N., Kousaka, H., Tokoroyama, T. (2016) Clarification of relationship between friction coefficient and transformed layer of CNx coating by in-situ spectroscopic analysis. Tribology International, 93, 660-665. https://doi.org/10.1016/j.triboint.2014.12.015
6. Chen, R., Tu, J.P., Liu, D.G. et al. (2012) Structural and mechanical properties of TaN/a-CN x multilayer films. Surface and Coatings Technology, 206(8-9), 2242-2248. https://doi.org/10.1016/j.surfcoat.2011.09.072
7. Wang, M., Toihara, T., Sakurai, M. et al. (2014) Surface morphology and tribological properties of DC sputtered nanoscale multilayered TiAlN/CNx coatings. Tribology International, 73, 36-46. https://doi.org/10.1016/j.triboint.2014.01.008
8. Contreras, E., Bolívar, F., Gómez, M.A. (2017) Influence of nitrogen variation on the microstructrual, mechanical and tribological properties of CNx coatings deposited by dc unbalanced magnetron sputtering. Surface and Coatings Technology, 332, 414-421. https://doi.org/10.1016/j.surfcoat.2017.05.095
9. Cui F.Z., Qing X.L., Li D.J., Zhao J. (2005) Biomedical investigations on CNx coating. Surface & Coating Technology, 200(1-4), 1009-1013. https://doi.org/10.1016/j.surfcoat.2005.02.157
10. Kovács, G.J., Veres, M., Koós, M., Radnóczi, G. (2008) Raman spectroscopic study of magnetron sputtered carbon-nickel and carbon nitride-nickel composite films: The effect of nickel on the atomic structure of the C/CNx matrix. Thin Solid Films, 516(21), 7910-7915. https://doi.org/10.1016/j.tsf.2008.04.081
11. Mubumbila, N., Tessier, P.-Y., Angleraud, B., Turban, G. (2002) Effect of nitrogen incorporation in CNx thin films deposited by RF magnetron sputtering. Surface and Coatings Technology, 151-152, 175-179. doi:10.1016/s0257- 8972(01)01569-9 https://doi.org/10.1016/S0257-8972(01)01569-9
12. Broitman, E., Czigány, Z., Greczynski, G. et al. (2010) Industrial-scale deposition of highly adherent CNx films on steel substrates. Surface and Coatings Technology, 204(21-22), 3349-3357. https://doi.org/10.1016/j.surfcoat.2010.03.038
13. Charitidis, C., Patsalas, P., Logothetidis, S. (2005) Effects of energetic species during the growth of nitrogenated amorphous carbon thin films on their nanomechanical properties. Thin Solid Films, 482(1-2), 177-182. https://doi.org/10.1016/j.tsf.2004.11.167
14. Tétard, F., Djemia, P., Angleraud, B. et al. (2002) Surface and bulk characterizations of CNx thin films made by r.f. magnetron sputtering. Surface and Coating Technolody, 151-152, 184-188. https://doi.org/10.1016/S0257-8972(01)01574-2
15. Gradowski, M.V., Ferrari, A.C., Ohr, R. et al. (2003) Resonant Raman characterisation of ultra-thin nano-protective carbon layers for magnetic storage devices. Ibid., 174-175, 246-252. https://doi.org/10.1016/S0257-8972(03)00602-9

Suggested Citation

Yu.S. Borysov, O.V. Volos, N.V. Vigilyanska, V.G. Zadoya, V.V. Strelchuk (2022) Influence of parameters of magnetron sputtering process on phase composition and structure of carbon nitride coatings. The Paton Welding J., 09, 15-20.