The Paton Welding Journal, 2023, #3, 20-25 pages
Electron beam surface melting of ingots of high-temperature titanium alloy VT9
O.M. Pikulin, S.V. Akhonin, V.O. Berezos, A.Yu. Severyn, O.G. Erokhin
E.O. Paton Electric Welding Institute of the NASU.
11 Kazymyr Malevych Str., 03150, Kyiv, Ukraine. E-mail: akhonin.sv@gmail.com
Abstract
Proceeding from the results of the performed package of research work, it was established that the chemical composition of metal in the surface-melted layer of high-temperature titanium alloy VT9 corresponds to standard requirements; and a lowering of aluminium content, an alloying element with vapour pressure higher, and an increase in the content of molybdenum and zirconium, alloying elements with vapour pressure lower than that of titanium, is observed. Investigations of the surface-melted layer showed that the depth of penetration of the surface layer in ingots of high-temperature titanium alloy VT9 of 600 mm diameter reaches 8 mm, the ingot surface is high-quality mirror-like with characteristic vacuum etching, even microrelief without cracks, tears or lacks-of-fusion, its roughness is in the range of 3…4 class at waviness of 0.2…0.6 mm. The surface-melted layer of the ingot has a finer structure, compared to base metal, and it consists of areas with isolated α-plates of 1.0…2.5 μm thickness, where the α-plates are gathered into colonies of 10…50 μm width, and the gaps between them are taken up by dispersed particles of 1…2 μm size, which can be the products of metastable phase decomposition. Ref. 13, Tabl. 1, Fig. 10.
products of metastable phase decomposition. Ref. 13, Tabl. 1, Fig. 10.
Keywords: high-temperature titanium alloy; ingot; surface defect; electron beam surface melting; chemical composition;
structure
Received: 02.12.2022
Accepted: 24.04.2023
References
1. Niinomi, M. (2011) Recent trends in titanium research and development in Japan. Proc. of 12th World Conf. on Titanium, 1, 30-37.
2. Bania, P. (1993) Beta titanium alloys and their role in the titanium industry. Beta Titanium Alloys in the 90's. TMS Publ., Warrendale, PA, 3-14.
3. Cui, C., Hu, B.M., Zhao, L., Liu, S. (2011) Titanium alloy production technology, market prospects and industry development. Mater. Des., 32, 1684-1691.
https://doi.org/10.1016/j.matdes.2010.09.0114. Babenko, E.P., Dolzhenkova, E.V. (2014) Investigation of the causes of destruction of a large-sized product made of VT23 alloy. Metallurgical and Mining Industry, 3, 82-85.
5. Khoreev, A.I. (2007) Theory and practice of development of titanium alloys for promising structures. Tekhnologiya Mashinostroeniya, 12, 5-13 [in Russian].
6. Antonyuk, S.L., Moyar, A.G., Kalinyuk A.N. et al. (2003) Titanium alloys for aircraft industry of Ukraine. Advances in Electrometallurgy, 1, 9-13.
7. Pikulin, A.N. (2016) Electron beam fusion of complexly-alloyed titanium alloys. Sovrem. Elektrometall., 3, 26-30 [in Russian].
https://doi.org/10.15407/sem2016.03.058. Koryagin, S.I., Pimenov, I.V., Khudyakov, V.K. (2000) Methods of treatment of materials: Manual. Kaliningrad, Kaliningr. University [in Russian].
9. Krivoukhov, V.A., Chubarov, A.D. (1990 Cutting of titanium alloys. Moscow, Mashinostroenie [in Russian].
10. Paton, B.E., Trigub, N.P., Akhonin, S.V., Zhuk, G.V. (2006) Electron beam melting of titanium. Kyiv, Naukova Dumka [in Russian].
11. Pavlova, T.V., Kashapov, O.S., Nochovnaya, N.A. (2012) Titanium alloys for gas turbine engines. All materials. Encyclopaedic Handbook [in Russian].
12. Khoreev, A.I., Khoreev, M.A. (2005) Titanium alloys, their application and prospects of development. Materialovedenie, 7, 25-34 [in Russian].
13. Aleksandrov, V.K., Anoshkin, N.F., Bochvar, G.A. et al. (1979) Semi-finished products from titanium alloys. Moscow, Metallurgiya [in Russian].
Suggested Citation
O.M. Pikulin, S.V. Akhonin, V.O. Berezos, A.Yu. Severyn, O.G. Erokhin (2023) Electron beam surface melting of ingots of high-temperature titanium alloy VT9.
The Paton Welding J., 03, 20-25.