CAUSE OF SECONDARY HARDENING IN Cr-Mo-V WELD METAL DURING LONG-TERM HEAT EXPOSURE

P. MOHYLA, I. HLAVATY and P. TOMCIK

Technical University of Ostrava, Czech Republic
 
 
Abstract
Results of microstructural analysis quantified changes in the dispersion phase in Cr-Mo-V weld metal during exposure in the sub-creep range are presented. The hypothesis that changes in the dispersion of MX particles during long-term heat exposure are significant has been confirmed by presented results.
 
 
Keywords: CrMoV steel welds, sub-creep range, secondary hardening, vanadium carbides and carbonitrides, microstructural analysis, image analysis
 
 
Received:                ??.??.??
Published:               28.02.11
 
 
References
1. Krejci, L. (2006) Mechanical testing of welded joints. In: Proc. of Seminar «Svarovaci den 2006». Ostrava: TU, 40-47.
2. Schmidova, E., Svanda, P., Vesely, D. et al. (2009). Mechanism of degradation of stabilised corrosion-resistant steel during the welding cycle. Anti-Corrosion Methods and Materials, 56(4), 206-217.
3. Bosela, M., Vinas, J., Varga, V. (2001) The analysis of welds-on with resistance against of high area pressure. In: Proc. of 9th Int. Sci. Conf. (Trnava, 25-26.10.2001). Bratislava: STU, 186-191.
4. Ashby, M.F., Ebeling, R. (1966) On the determination of the number, size, spacing and volume fraction of spherical second-phase particles from extraction replicas. Transact. of Metallurgical Society of AIME, 236.
5. Prnka, T. (1975) Diss. for Technical University of Ostrava.
6. Purmensky, J. (1978) Diss. for Technical University of Ostrava.
7. Kelly, A., Nicholson, R.B. (1963) Precipitation hardening. Progress in Material Sci., 10.
8. Ashby, M.F. (1969) Physics of strength and plasticity. MIT Press, 113.

---