COMPARATIVE EVALUATION OF SENSITIVITY OF WELDED JOINTS ON ALLOY INCONEL 690 TO HOT CRACKING

K.A. YUSHCHENKO, V.S. SAVCHENKO, N.O. CHERVYAKOV, A.V. ZVYAGINTSEVA, G.G. MONKO and V.A. PESTOV

E.O. Paton Electric Welding Institute, NASU, Kiev, Ukraine
 
 
Abstract
Sensitivity of metal of the welds made with wires Inconel^® 52 and Inconel^® 52MSS to hot cracking was evaluated. The machine testing methods (Varestraint-Test and PVR-Test), which provide for forced deformation of test specimens during welding, were used. The welds made with wire Inconel 52MSS were shown to be more resistant to ductility dip cracking, but several times more sensitive to solidification cracking. Evaluation of ductile properties of the weld metal using the «Ala-Too» machine showed that the Inconel 52MSS type weld metal had no ductility dip, whereas the Inconel 52 type weld metal was characterized by a pronounced decrease in the elongation values.
 
 
Keywords: TIG welding, nickel alloys, filler wire, weld metal, evaluation of crack resistance, ductility dip range, grain boundary, forced deformation
 
 
Received:                ??.??.??
Published:               28.11.11
 
 
References
1. Hemsworth, W., Boniszewski, T., Eaton, N.F. (1969) Classification and definition of high temperature welding cracks in alloys. Metal Constr. and British Welding J., 1, 25, 5-16.
2. Torres, E.A., Peternella, F.G., Caram, R. et al. (2010) In situ scanning electron microscopy high temperature deformation experiments to study ductility dip cracking of Ni-Cr-Fe alloys. In: In situ studies with phonons, neutrons and scattering. Berlin; Heidelberg: Springer, 27-39.
3. Lippold, J.C., Kotecki, D.J. (2005) Welding metallurgy and weldability of stainless steels. John Wiley & Sons.
4. Collins, M.G., Lippold, J.C. (2003) An investigation of ductility dip cracking in nickel-based weld metals. Pt I. Welding J., 82(10), 288-295.
5. Collins, M.G., Ramirez, A.J., Lippold, J.C. (2003) An investigation of ductility dip cracking in nickel-based weld metals. Pt II. Ibid., 82(10), 348-354.
6. Collins, M.G., Ramirez, A.J., Lippold, J.C. (2004) An investigation of ductility dip cracking in nickel-based weld metals. Pt III. Ibid., 83(2), 39-49.
7. Lippold, J.C., Nissley, N.E. (2007) Further investigation of ductility dip cracking in high chromium, nickel-based filler metals. Welding in the World, 51(9/10), 24-30.
8. Noecker, F.F., DuPont, J.N. (2009) Metallurgical investigation into ductility dip cracking in nickel-based alloys. Pt II. Welding J., 88(3), 62-77.
9. Cross, C.E., Coniglio, N. (2008) Weld solidification cracking: critical conditions for crack initiation and crowth. In: Hot cracking phenomena in welds II. Berlin; Heidelberg: Springer.
10. Zvyagintseva, A.V., Yushchenko, K.A., Savchenko, V.S. (2001) Effect of structural changes in high-temperature heating on ductile characteristics of nickel alloys. The Paton Welding J., 4, 13-17.
11. Herold, H., Hubner, A., Zinke, M. (2004) Investigation of the use of nitrogenous shielding gas in welding and its influence on the hot-crack behaviour of high temperature resistant fully austenitic Ni- and Fe-base alloys. IIW Doc. IX-2110-04.
12. Yushchenko, K.A., Savchenko, V.S. (2008) Classification and mechanisms of cracking in welding high-alloy steels and nickel alloys in brittle temperature ranges. In: Hot cracking phenomena in welds II. Berlin; Heidelberg: Springer, 95-114.
13. Vallant, R., Cerjak, H. (2004) Investigation on the mechanical values and the hot crack susceptibility of Ni-base weld metals type 70/20 and 70/15 of different Nb contents. IIW Doc. II-1535-04.
14. Savage, W.F., Lundin, C.D. (1965) The Varestraint test. Welding J., 44(10), 433-442.
15. Savchenko, V.S., Yushchenko, K.A. (1993) Mechanism of formation and ways of prevention of underbead cracks in welding of austenitic steels. Avtomatich. Svarka, 12, 8-11.
16. Yushchenko, K.A., Savchenko, V.S., Chervyakov, N.O. et al. (2010) Probable mechanism of cracking of stable-austenitic welds caused by oxygen segregation. The Paton Welding J., 5, 5-9.
17. Trefilov, V.I., Majboroda, V.P., Firstov, S.A. et al. (1986) Investigation of influence of localised shear deformation on composition of surface steel fractured in vacuum. Metallofizika, 8(3), 78-83.

---

Suggested Citation

K.A. YUSHCHENKO, V.S. SAVCHENKO, N.O. CHERVYAKOV, A.V. ZVYAGINTSEVA, G.G. MONKO and V.A. PESTOV (2011) COMPARATIVE EVALUATION OF SENSITIVITY OF WELDED JOINTS ON ALLOY INCONEL 690 TO HOT CRACKING. The Paton Welding J., 11, 2-7.

---