Automatic Welding 2022 #05
Avtomaticheskaya Svarka (Automatic Welding), #5, 2022, pp. 16-21

Technological features of welding 30KHGSN2A steel

L.M. Lobanov, P.V. Goncharov, V.D. Poznyakov, O.A. Gaivoronsky, A.V. Zavdoveev

E.O. Paton Electric Welding Institute of the NAS of Ukraine. 11 Kazymyr Malevych Str., 03150, Kyiv, Ukraine. E-mail: office@paton.kiev.ua

High-strength alloy steels of 30KhGSN2A type are widely used in the manufacture of products that can bear signifi cant loads. In the thermally hardened state, this steel has a tensile strength of more than 1500 MPa. Depending on the product, it can be used in thicknesses from 2 to 15 mm and more. However, the use of such steels requires strict technical requirements for their heat treatment, creating diffi culties during the manufacture of products. Development of welding technology in the manufacture of products of 30KhGSN2A steel is currently relevant. In the present work, technological features of welding of high-strength alloy steels of 30KhGSN2A type are stated. 14 Ref., 6 Tabl., 6 Fig.
Keywords: high-strength steels, pulsed-arc welding, heat-aff ected zone, structure, mechanical properties, austenitic welding materials

Received: 07.04.2022


1. Sterenbogen, Yu.A., Vasiliev, D.V., Demchenko, E.L., Novikova, D.P. (2006) Role of peak stresses in formation of cold cracks in welded joints of hardenable steels. The Paton Welding J., 4, 636, 11-20.
2. Kulik, V.M., Vasiliev, V.G., Grigorenko, G.M. et al. (2007) Phase and structural transformations in welding and arc treatment of 30KhGSA steel joints. The Paton Welding J., 9, 653, 10-15.
3. Kulik, V.M., Savitsky, M.M., Lupan, A.F. et al. (2007) Nonconsumable electrode combined welding of shaft billets. In: Proc. of 2nd Sci.-Techn. Seminar on Welding and Related Technologies in Industry [яка мова?
4. Sun, Qing Jie, Hai Feng Hu, Xin Yuan, Ji Cai Feng. (2011) Research status and development trend of narrow-Gap TIG welding. Advanced Materials Research, 308, 1170-1176. Trans Tech Publications Ltd. https://doi.org/10.4028/www.scientific.net/AMR.308-310.1170
5. Krzywy, Kamil Sebastian (2016) Application of the isothermal quenching for formation of the mechanical properties of structural steel 30HGSNA (30CrMnSiNi). PhD diss., Zakład Inżynierii Powierzchni.
6. Pietruszka, J. (2003) Full scale fatigue tests of the commuter aircraft under-carriage made of high strength low-alloy steel. Prace Instytutu Lotnictwa, 1-2 (172-173), 28-31.
7. Dementiev, V.B., Zasypkin, A.D. (2015) Investigation of structure and mechanical properties of 30KhGSN2A steel in technologies of piercing, reducing and high-temperature thermomechanical treatment of extra-thick-walled pipe billets. Khimicheskaya Fizika i Mezoskopiya, 17(3), 372-379 [in Russian].
8. Skuratov, D.L., Evdokimov D.V., Fedorov D.G. (2014) Research of thermal cycle parameters and surface condition of the samples from high-tension steel 30ХГСН2А at cylindrical external grinding. Life Sci. J., 11(10), 678-681.
9. Gajvoronsky, A.A. (2013) Influence of diffusible hydrogen on delayed cracking resistance of high-carbon steel welded joints. The Paton Welding J., 5, 721, 15-21.
10. Gajvoronsky, A.A. (2014) Resistance to cold crack formation of HAZ metal of welded joint on high-strength carbon steels. The Paton Welding J., 2, 729, 3-12. https://doi.org/10.15407/tpwj2014.02.01
11. Poznyakov, V.D., Kostin, V.A., Gajvoronsky, A.A. et al. (2015) Effect of welding thermal cycle on structure-phase transformations and properties of HAZ metal of alloyed 30Kh2N2MF type medium-carbon steel. The Paton Welding J., 2, 8-15. https://doi.org/10.15407/tpwj2015.02.02
12. Marek, S., Bień, A., Stanisławska, A. (2021) Laser beam as a precision tool to increase fatigue resistance in an eyelet of undercarriage drag strut. Int. J. of Precision Engineering and Manufacturing-Green Technology, 1-16.
13. Łunarska, E., Nikiforow, K., Sitko, E. (2003) Improving the resistance to stress corrosion cracking and to hydrogen embrittlement of bainite high strength steel. Advances in Materials Sci. 3, 2(4), 35-41.
14. Kulik, V.M., Vasiliev, V.G. (2006) Variations in structure and properties of HAZ metal in welded joints on theel 30KhGSA in arc treatment. The Paton Welding J., 7, 639, 19-25.

Advertising in this issue: