HYDROGEN BEHAVIOUR IN REPAIR WELDING OF THE MAIN PIPELINES UNDER PRESSURE

V.I. MAKHNENKO, O.I. OLEJNIK and A.P. PALTSEVICH


E.O. Paton Electric Welding Institute, NASU, Kiev, Ukraine
 
 
Abstract
Possibility of diffusion hydrogen penetration from hydrocarbon gas transported through the gas pipeline during repair welding performance on an operating pipeline has been analyzed. It is shown that at partial pressure of diffusion hydrogen on the inner surface of steel pipe in the range of 0.10-0.75 MPa at residual wall thickness in the defect zone of more than 5 mm increase of the parameter of hydrogen (cold) cracking risk is not higher than 5-11 %. Values of experimental measurements of diffusion hydrogen flow through the pipe wall in operating pipelines are given.
 
 
Keywords: repair arc welding, operating gas pipelines, diffusion hydrogen, gas pipeline wall, hydrogen cracks, risk of formation
 
 
Received:                ??.??.??
Published:               28.09.11
 
 
References
1. Makhnenko, V.I., Korolova, T.V., Lavrynets, I.G. (2002) Numerical study of the effect of microstructural transformation on hydrogen redistribution in fusion welding of structural steels. In: Mathematical modelling of weld phenomena. Ed. by H. Cerjak. London: Maney Publ., 903-923.
2. Katz, D.L. (1965) Guideline on recovery, transport and processing of natural gas. Moscow: Nedra.
3. Makhnenko, V.I., Korolyova, T.V., Lavrinets, I.G. (2002) Effect of microstructural transformations on redistribution of hydrogen in fusion welding of structural steels. The Paton Welding J., 2, 6-13.
4. Nechaev, Yu.S. (2008) Physical complex problems of ageing, embrittlement and fracture of metallic materials of hydrogen power engineering and main gas pipelines. Uspekhi Fizich. Nauk, 178(7), 709-726.
5. Makhnenko, V.I. (2006) Safe service life of welded joints and assemblies of current structures. Kiev: Naukova Dumka.
6. Seyffarth, P., Meyer, B., Scharff, A. (1992) Grosser Atlas Schweiss-ZTU-Schaubilder. Duesseldorf: DVS.
7. (1998) Welding Handbook. Vol. 4: Materials and application. Pt 2. 8th ed. Miami: AWS.
8. Petrov, G.L., Million, A. (1964) Processes of hydrogen redistribution in welded joints of carbon and low-alloy steels. Svarochn. Proizvodstvo, 10, 1-6.

Suggested Citation

V.I. MAKHNENKO, O.I. OLEJNIK and A.P. PALTSEVICH (2011) HYDROGEN BEHAVIOUR IN REPAIR WELDING OF THE MAIN PIPELINES UNDER PRESSURE. The Paton Welding J., 09, 2-9.