TPWJ, 2014, #6-7, 139-142 pages
ELECTRODES FOR WELDING OF DISSIMILAR CHROMIUM MARTENSITIC AND CHROMIUM-NICKEL AUSTENITIC STEELS
Journal The Paton Welding Journal
Publisher International Association «Welding»
ISSN 0957-798X (print)
Issue № 6-7, 2014 (June-July)
L.S. ZAKHAROV, A.R. GAVRIK and V.N. LIPODAEV
E.O. Paton Electric Welding Institute, NASU. 11 Bozhenko Str., 03680, Kiev, Ukraine. E-mail: firstname.lastname@example.org
Carried are the investigations on development of low-carbon chromium electrodes of 05Kh6MF type. Effect of coating composition on carbon content in deposited metal of Kh6M type was investigated. It is determined that joint introduction of chromium and zirconium oxides in 5-10 wt.% amount at simultaneous removal of marble from the coating is the most efficient for carbon reduction. Slag system of fluoride-magnesium oxide type coating was developed, providing reduction of carbon content in the deposited metal to 0.04-0.06wt.% at sufficiently low content of diffusible hydrogen. Electrodes of ANL-10 grade for welding of dissimilar joints of chromium martensitic steels of 10Kh9NMFB type and chromium-nickel austenitic steels of 10Kh18N10T type were developed on its basis. The electrodes provide for stable arcing, insignificant spattering, good weld formation in all spatial positions and easy separation of slag crust. 12 Ref., 3 Tables, 2 Figures.
arc welding, dissimilar steels, coated electrodes, deposited metal, carbon reduction, diffusible hydrogen, welding-technological properties
1. Skulsky, V.Yu., Tsaryuk, A.K. (2004) New heat-resistant steels for manufacture of weldments in heat power units (Review). The Paton Welding J., 4, 32-37.
2. Skulsky, V.Yu. (2005) Metal structure in the fusion zone and HAZ of welded joints on high-chromium heat-resistant steels. Ibid., 5, 10-18.
3. Erokhin, A.A. (1964) Kinetics of metallurgical processes of arc welding. Moscow: Mashinostroenie.
4. Erokhin, A.A., Kuznetsov, O.M. (1959) Electrodes with nonoxidation coating. Svarochn. Proizvodstvo, 12, 1-4.
5. Erokhin, A.A., Kuznetsov, O.M. (1961) Decrease in carbon content in weld metal during welding of stainless steels. Avtomatich. Svarka, 11, 1-4.
6. Sokolov, E.V., Sidlin, Z.A., Vagapov, I.M. (1968) Development of electrodes providing low carbon content in deposited metal of austenite class. In: Welding of structures from high-alloy steels. Leningrad: LDNTP.
7. Kakhovsky, N.I., Lipodaev, V.N. (1968) Electrodes for welding of chrome-nickel stainless steel of 18-10 type with low carbon content. Avtomatich. Svarka, 12, 8-10.
8. Kakhovsky, N.I., Lipodaev, V.N., Kakhovsky, Yu.N. (1970) Decrease in carbon content in weld metal during manual arc welding of stainless steels. Ibid., 6, 8-10.
9. Knunyants, I.L. (1967) Concise chemical encyclopedia. Moscow: Sov. Entsycl.
10. Rode, T.V. (1962) Oxygen chromium compounds and chromium catalyzers. Moscow: AN SSSR.
11. Kakhovsky, N.I., Lipodaev, V.N., Zakharov, L.S. (1977) Decrease of carbon content in weld metal by high-temperature baking of electrode coating components. Avtomatich. Svarka, 2, 8-10.
12. Potapov, N.I. (1985) Oxidation of metals in fusion welding. Moscow: Mashinostroenie.