INVESTIGATION OF СRACKING SUSCEPTIBILITY OF AUSTENITIC MATERIAL USING PVR-TEST PROCEDURE

K.A. YUSHCHENKO, V.S. SAVCHENKO, N.O. CHERVYAKOV, A.V. ZVYAGINTSEVA, G.G. MONKO and V.A. PESTOV


E.O. Paton Electric Welding Institute, NASU. 11 Bozhenko Str., 03680, Kiev, Ukraine. E-mail: office@paton.kiev.ua
 
 
Abstract
Comparative investigation of hot cracking sensitivity of commercial welding wires has been performed. It is shown that an all-purpose method of weldability evaluation can be the machine method with controllable forced deformation during TIG welding (PVR-test method), which allows separating the conditions of initiation of solidification cracks and ductility dip cracks in the weld and HAZ metal, and provides comprehensive information about quantitative characteristics of cracking sensitivity. 6 Ref., 9 Figures.
 
 
Keywords: weldability, hot cracks, crack resistance evaluation, high-alloyed steels, nickel alloys
 
 
Received:                11.04.14
Published:               28.09.14
 
 
References
1. ISO 17641-1:2004: Destructive tests on welds in metallic materials. Hot cracking tests for weldments. Arc welding processes. Pt 1: General.
2. Hemsworth, W., Boniszewski, T., Eaton, N.F. (1969) Classification and definition of high temperature welding cracks in alloys. Metal Constr. and British Welding J., 1(25), 5-16.
3. Lippold, J.C., Kotecki, D.J. (2005) Welding metallurgy and weldability of stainless steels. Jonh Wiley&Sons.
4. Derlomenko, V.V., Yushchenko, K.A., Savchenko, V.S. et al. (2010) Technological strength and analysis of causes of weldability deterioration and cracking. The Paton Welding J., 9, 20-23.
5. ISO/TR 17641-3:2005: Destructive tests on welds in metallic materials. Hot cracking tests for weldments. Arc welding processes. Pt 3: Externally loaded tests.
6. Herold, H., Streitenberger, M., Pchennikov, A. (2000) Modelling of the PVR-test to examine the origin of different hot cracking types. IIW Doc. IX-H-474-00.

Suggested Citation

K.A. YUSHCHENKO, V.S. SAVCHENKO, N.O. CHERVYAKOV, A.V. ZVYAGINTSEVA, G.G. MONKO and V.A. PESTOV (2014) INVESTIGATION OF СRACKING SUSCEPTIBILITY OF AUSTENITIC MATERIAL USING PVR-TEST PROCEDURE. The Paton Welding J., 06, 10-13.